ZnO/ZnS heterostructures for hydrogen production by photoelectrochemical water splitting
2016
This work studies the photoelectrochemical behavior of novel ZnO/ZnS heterostructures obtained by means of anodization in water and glycerol/water/NH4F electrolytes with different Na2S additions under controlled hydrodynamic conditions. For this purpose different techniques such as Field Emission Scanning Electronic Microscopy (FE-SEM) with EDX, Raman spectroscopy and photoelectrochemical water splitting tests under standard AM 1.5 conditions have been carried out. The obtained results showed that the hydrodynamic conditions promoted an ordered nanotubular morphology which facilitates electron-hole separation and consequently, the photoelectrochemical activity for water splitting is enhance…
Influence of annealing atmosphere on photoelectrochemical response of TiO2 nanotubes anodized under controlled hydrodynamic conditions
2021
[EN] The influence of three annealing atmospheres (air, nitrogen and argon) and the use of controlled hydrodynamic conditions (from 0 to 5000 rpm) on morphological, structural, chemical and photoelectrochemical properties of TiO2 nanotubes have been evaluated. For this purpose, different characterization techniques have been used: Field Emission Scanning Electron Microscopy, Raman Confocal Laser Spectroscopy, X-Ray Diffraction, X-Ray Photoelectron Spectroscopy, Incident Photon-to-electron Conversion Efficiency measurements, ultraviolet-visible absorption spectra, Mott-Schottky analysis and photoelectrochemical water splitting tests. According to the results, it can be concluded that both hy…
Effect of Reynolds number and lithium cation insertion on titanium anodization
2016
This work studies the influence of using hydrodynamic conditions (Reynolds number, Re = 0 to Re = 600) during Ti anodization and Li+ intercalation on anatase TiO2 nanotubes. The synthesized photocatalysts were characterized by using Field Emission Scanning Electron Microscope (FE-SEM), Raman Confocal Laser Microscopy, Electrochemical Impedance Spectroscopy (EIS), Mott-Schottky analysis (M-S), photoelectrochemical hydrogen production and resistance to photocorrosion tests. The obtained results showed that the conductivity of the NTs increases with Li+ intercalation and Re. The latter is due to the fact that the hydrodynamic conditions eliminate part of the initiation layer formed over the tu…
Redshift of absorption threshold of TiO2 Nanotubes due to Cu2O electrodeposition
2013
Electronic Properties of Thermal Oxides on Ti and Their Influence on Impedance and Photoelectrochemical Behavior of TiO2 Nanotubes
2017
Thermal oxidation of titaniumwas carried out at 350◦C, 450◦C, and 550◦C for 2 h or 12 h.X-rayDiffraction and Raman Spectroscopy suggest that the thermal oxides are scarcely crystallinewhen the annealing temperature is low, while both anatase and rutile are present for high annealing temperature and time. Photoelectrochemical measurements allowed estimation of a bandgap decreasing from 3.35 eV to 3.15 eV with increasing annealing temperature. The impedance spectra confirmed the formation of n-type semiconductors, with an impedance strongly decreasing on going from a reverse bias toward a forward bias regime. TiO2 nanotubes grown by anodizing Ti in NH4F and water containing ethylene glycol so…
The effect of Annealing Conditions on the Impedance and on the Photoelectrochemical behavior of TiO2 Nanotubes
2015
Titanium oxide nanotubes (NTs) have attracted much attention during last decade due to their special characteristics such as one-dimensional highly ordered geometry with large surface area and good chemical and optical stability.
Synergistic effect between hydrodynamic conditions during Ti anodization and acidic treatment on the photoelectric properties of TiO2 nanotubes
2015
In the present work, the combined influence of controlled hydrodynamic conditions during Ti anodization and the acidic treatment with HClO4 on the photoelectric properties of mixed anatase/rutile TiO2 nanotubes has been studied. Anodized samples were analyzed by means of Field Emission Scanning Electronic Microscopy (FE-SEM), Confocal Raman Microscopy, electrochemical measurements (electrochemical impedance spectroscopy and Mott-Schottky analysis) and photoelectrochemical measurements. It has been observed that the use of hydrodynamic conditions increases the surface area of nanotubes, while acidic treatment enhances their conductivity. Besides, there is a clear synergistic effect between t…
Photoelectrochemical characterization of Cu2O-nanowire arrays electrodeposited into anodic alumina membranes
2007
Perfectly aligned nanowire arrays of polycrystalline Cu2O were grown by template-pulsed electrodeposition from a cupric acetate-sodium acetate bath into anodic alumina membranes (AAM). The photoelectrochemical behavior of arrays with different nanowire lengths (0.5 mu m and 2 mu m) was investigated in neutral solution, and the results compared to those pertaining to Cu2O films grown with the same procedure. Although all samples displayed the same indirect bandgap (similar to 1.9 eV), differences were observed both in photocurrent intensity and sign. The latter changed with potential and wavelength in different ways for nanowires and films, revealing a different defect concentration in the t…
Photoelectrochemical Evidence of Cu2O/TiO2 Nanotubes Hetero-Junctions formation and their Physicochemical Characterization
2014
Cu2O/TiO2 nanotubes heterojunctions were fabricated by electrochemical deposition of cuprous oxide on TiO2 nanotubes arrays grown by anodizing. X-ray diffraction and Raman Spectroscopy analysis allows for identification of Cu2O, whose morphological features were studied by Scanning Electron Microscopy as a function of the charge circulated during the electrodeposition step. Photoelectrochemical measurements in aqueous solutions evidenced a red shift of the light absorption threshold of TiO2 nanotubes due to the presence of cuprous oxide even for very low circulated charges, while electrochemical impedance measurements proved a significant reduction of the electrode impedance due the presenc…